            note = {Tin(IV) chloride pentahydrate (SnCl{$_4$}?5H{$_2$}O) is a hydrated compound of
tin(IV) chloride (SnCl{$_4$}), in the form of crystals that are water-soluble and
hygroscopic. SnCl{$_4$}?5H{$_2$}O is stable under normal environmental conditions and is
used in various industrial applications, such as a catalyst in the synthesis of organic
compounds, including esterification. This study aims to determine the effects of
water flow rate, SnCl{$_4$} : H{$_2$}O mole ratio, and air addition on the crystallization rate,
temperature profile, and reaction heat, as well as the optimal formulation and
process conditions for the formation of SnCl{$_4$}?5H{$_2$}O crystals. The research stages
included preparation of tools and materials, synthesis of SnCl{$_4$}?5H{$_2$}O with and
without additional air supply, analysis of crystallization rate, and mass and energy
balances. The results showed that decreasing the water flow rate increased the
crystallization rate and lowered the maximum reaction temperature. Increasing the
SnCl{$_4$} : 5H{$_2$}O mole ratio also enhanced the crystallization rate but reduced the
maximum temperature. Additional air supply accelerated cooling but decreased
crystallization efficiency. The best synthesis condition was achieved at a 2 : 7,8
mole ratio, 0.0041 mL/s flow rate, and stirring, resulting in 89.09\% conversion, a
crystallization rate of 0.000285 g/s, and a maximum temperature of 48?C.},
           month = {March},
          school = {Fakultas Teknik Universitas Sultan Ageng Tirtayasa},
            year = {2026},
           title = {SINTESIS DAN KARAKTERISASI TIMAH TETRAKLORIDA PENTAHIDRAT (SnCl4.5H2O) UNTUK MENDUKUNG HILIRISASI PRODUK BERBASIS TIMAH},
        keywords = {crystallization rate, synthesis, SnCl{$_4$}, SnCl{$_4$}?5H{$_2$}O, tin 
laju kristalisasi, sintesis, SnCl{$_4$}, SnCl{$_4$}?5H{$_2$}O, timah},
             url = {https://eprints.untirta.ac.id/58681/},
        abstract = {Timah tetraklorida pentahidrat (SnCl{$_4$}?5H{$_2$}O) adalah senyawa hidrat dari Timah tetraklorida (SnCl{$_4$}), suatu senyawa anorganik berbentuk kristal yang larut dalam air dan bersifat higroskopis. Dalam bentuk hidratnya, SnCl{$_4$}?5H{$_2$}O stabil pada kondisi lingkungan biasa dan digunakan dalam berbagai aplikasi industri. Salah satu penggunaannya adalah sebagai katalis dalam sintesis senyawa organik, seperti esterifikasi dan reaksi Friedel-Crafts. Selain itu, SnCl{$_4$}?5H{$_2$}O juga dimanfaatkan dalam pembuatan bahan semikonduktor dan sebagai prekursor dalam produksi film tipis oksida timah untuk aplikasi elektronik. Sifatnya yang multifungsi menjadikan SnCl{$_4$}?5H{$_2$}O komponen penting dalam industri kimia, elektronik, dan material canggih. Tujuan dari penelitian ini yaitu membuat kristal SnCl{$_4$}?5H{$_2$}O yang memiliki kualitas yang baik, menemukan kondisi proses sintesis terbaik untuk meningkatkan kualitas dan konsistensi pembentukan kristal SnCl{$_4$}?5H{$_2$}O dan mengetahui karakteristik kristal SnCl{$_4$}?5H{$_2$}O yang dihasilkan dari proses sintesis dengan variasi kondisi yang berbeda.. Tahapan dari penelitian ini meliputi preparasi sampel, reaksi hidrolisis, uji karakteristik SnCl4 dan analisis neraca massa. Hasil yang didapatkan yaitu berupa nilai pembentukkan kristal terbesar yaitu 90.73\% pada sampel 4 dengan rasio reaktan 5 : 3.}
}