eprintid: 51843
rev_number: 16
eprint_status: archive
userid: 5622
dir: disk0/00/05/18/43
datestamp: 2025-07-17 08:08:04
lastmod: 2025-07-17 08:08:04
status_changed: 2025-07-17 08:08:04
type: thesis
metadata_visibility: show
creators_name: Ningthyas, Dita Azzahra Rai
creators_name: Dini, Rizkika Amalia
creators_id: 3335210037
creators_id: 3335210039
contributors_type: http://www.loc.gov/loc.terms/relators/THS
contributors_type: http://www.loc.gov/loc.terms/relators/THS
contributors_name: Rahmayetty, Rahmayetty
contributors_name: Sari, Denni Kartika
contributors_id: 197410021999032003
contributors_id: 198110042008122003
corp_creators: UNIVERSITAS SULTAN AGENG TIRTAYASA
corp_creators: FAKULTAS TEKNIK
corp_creators: JURUSAN TEKNIK KIMIA
title: ISOLASI CELLULOSE MICROFIBRILS (CMF) DARI PADINA SP. MENGGUNAKAN METODE HIDROLISIS ASAM
ispublished: pub
subjects: QD
divisions: FT
divisions: TekKimia
full_text_status: restricted
note: Indonesia memiliki potensi besar dalam pemanfaatan rumput laut, termasuk Padina sp. sebagai sumber selulosa. Cellulose Microfibrils (CMF) memiliki karakteristik, antara lain memiliki luas permukaan spesifik, kekuatan dan kekakuan yang tinggi, memiliki berat yang rendah, bersifat biodegradable dan renewable. CMF dapat diaplikasikan pada industri komposit, otomotif, pulp dan kertas, elektronik, cat dan coating, dan lain-lain. Penelitian ini bertujuan untuk mengetahui kadar dan %yield selulosa yang dihasilkan dari proses alkalinasi dan pemutihan, serta untuk mengetahui ukuran partikel Cellulose Microfibrils (CMF) yang dihasilkan pada metode hidrolisis asam.. Penelitian ini diawali dengan menghaluskan dan menyaring Padina sp., dilanjutkan dengan alkalinasi menggunakan NaOH 0,5 M dan pemutihan dengan H₂O₂ 12% untuk memperoleh selulosa. Selanjutnya, selulosa dihidrolisis menggunakan asam sulfat (H₂SO₄) dengan dengan variasi konsentrasi 40; 45; 50; 55; dan 60% untuk menghasilkan Cellulose Microfibrils (CMF). Hasil menunjukkan peningkatan kadar selulosa dari 26,93% menjadi 63,47% setelah perlakuan, dengan %yield sebesar 38,26%. Analisis Ukuran CMF hidrolisis H2SO4 50% menggunakan Dino-Lite menunjukkan bentuk yang tidak teratur dan cenderung menyerupai serpihan yang tampak memanjang dan tipis dengan rata-rata panjang partikel adalah 0,7966 mm dan rata-rata luas area adalah 0,0299 mm².
abstract: Indonesia has significant potential in utilizing seaweed, including Padina sp., as a source of cellulose. Cellulose Microfibrils (CMF) possess desirable characteristics such as high specific surface area, high strength and stiffness, low weight, and are both biodegradable and renewable. CMF can be applied in various industries, including composites, automotive, pulp and paper, electronics, paints, and coatings. This study aimed to determine the cellulose content and yield obtained through alkalization and bleaching processes, as well as the particle size of CMF produced via acid hydrolysis. The process began with grinding and sieving Padina sp., followed by treatment with 0.5 M NaOH for alkalization and 12% H₂O₂ for bleaching to extract cellulose. The extracted cellulose was then hydrolyzed using sulfuric acid (H₂SO₄) at varying concentrations of 40%, 45%, 50%, 55%, and 60% to produce CMF. Results showed that cellulose content increased from 26.93% to 63.47% after treatment, with a yield of 38.26%. Analysis using Dino-Lite for CMF obtained from 50% H₂SO₄ hydrolysis revealed irregular, elongated, and thin flake-like particles, with an average length of 0.7966 mm and an average surface area of 0.0299 mm²
date: 2025-07-16
date_type: published
pages: 63
institution: Fakultas Teknik Universitas Sultan Ageng Tirtayasa
department: TEKNIK KIMIA
thesis_type: sarjana
thesis_name: sarjana
citation:   Ningthyas, Dita Azzahra Rai and Dini, Rizkika Amalia  (2025) ISOLASI CELLULOSE MICROFIBRILS (CMF) DARI PADINA SP. MENGGUNAKAN METODE HIDROLISIS ASAM.  S1 thesis, Fakultas Teknik Universitas Sultan Ageng Tirtayasa.   
document_url: https://eprints.untirta.ac.id/51843/1/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_Fulltext.pdf
document_url: https://eprints.untirta.ac.id/51843/2/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_01.pdf
document_url: https://eprints.untirta.ac.id/51843/3/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_02.pdf
document_url: https://eprints.untirta.ac.id/51843/4/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_03.pdf
document_url: https://eprints.untirta.ac.id/51843/5/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_04.pdf
document_url: https://eprints.untirta.ac.id/51843/6/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_05.pdf
document_url: https://eprints.untirta.ac.id/51843/7/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_Ref.pdf
document_url: https://eprints.untirta.ac.id/51843/8/Dita%20Azzahra%20Rai%20Ningthyas_3335210037_Lamp.pdf