            note = {Penelitian ini bertujuan untuk mensintesis carbon dots (C-dots) dari limbah kulit pepaya menggunakan metode iradiasi gelombang mikro (microwave) dan mengkaji potensinya sebagai sensor ion logam Fe?{$^+$}. Sintesis dilakukan dengan cara menghaluskan kulit pepaya dan memanaskannya menggunakan microwave, kemudian dilakukan karakterisasi menggunakan spektrofotometer UV-Vis dan photoluminescence (PL). Hasil pengamatan menunjukkan bahwa C-dots yang dihasilkan memiliki pendaran cahaya berwarna cyan saat disinari sinar UV, dengan puncak emisi pada rentang 420?490 nm. Analisis UV-Vis menunjukkan adanya perubahan spektrum absorbansi setelah penambahan Fe?{$^+$}, sedangkan analisis PL menunjukkan perubahan intensitas emisi yang menandakan interaksi spesifik antara C-dots dan ion Fe?{$^+$}. Berdasarkan hasil tersebut, C-dots dari kulit pepaya memiliki potensi sebagai material sensor optik yang sensitif dan ramah lingkungan untuk mendeteksi logam berat Fe?{$^+$}.},
            year = {2025},
           title = {DETEKTOR LOGAM Fe3+ DARI CARBON DOTS LIMBAH KULIT PEPAYA MENGGUNAKAN TEKNIK MICROWAVE},
        keywords = {Carbon Dots, Fe3+, Microwave, Papaya Peel
Carbon Dots, Fe?{$^+$}, Kulit Pepaya, Microwave},
             url = {https://eprints.untirta.ac.id/51091/},
        abstract = {This study aims to synthesize carbon dots (C-dots) from papaya peel waste using microwave irradiation method and assess their potential as Fe?{$^+$} metal ion sensor.  The synthesis was carried out by smoothing papaya skin and heating it using microwave, then characterization was carried out using UV-Vis spectrophotometer and photoluminescence (PL). The results showed that the Cdots produced had a cyan-colored luminescence when illuminated by UV light, with emission peaks in the range of 420-490 nm. UV-Vis analysis showed a change in absorbance spectrum after the addition of Fe?{$^+$}, while PL analysis showed a change in emission intensity indicating a specific interaction between Cdots and Fe?{$^+$} ions. Based on these results, C-dots from papaya skin have the potential as a sensitive and environmentally friendly optical sensor material to detect Fe?{$^+$} heavy metal.}
}