title: STUDI PERLAKUAN CURING PADA PAPAN PARTIKEL   BIODEGRADABLE PELEPAH KELAPA SAWIT   BERPENGUAT MESOKARP
creator: Husein, Saddam
subject: TJ Mechanical engineering and machinery
subject: TS Manufactures
description: The increase in oil palm plantations in Indonesia is growing every year, causing the need for innovation in the treatment of waste from oil palm. Particle board is one of the innovations processed from palm oil waste. This study aims to evaluate and determine the effect of curing treatment on the quality of biodegradable particle board  to meet SNI 03-2105-2006 standards. The preparation of samples in this study began by mixing  15% mesocarp fiber, 50% filler from palm stems, PVA-c matrix and epoxy resin 25% and 10% respectively. After that, it was printed with a compaction pressure of 30 bar for 120 minutes and a curing treatment  was carried out with variable without curing treatment, curing temperature 75°C and curing temperature 150°C.  The tests in this study are divided into two, namely, testing physical properties (density, moisture content, thickness development and water absorption) and testing mechanical properties (bending strength and modulus of elasticity). Based on the test results, T3 sample has the best desity value of 0.81 gr/cm3. The moisture content test obtained the best value in the T3 sample with a value of 4.4%. In the thick development test, the best value was obtained in the T3 sample of 4.9%. Likewise, the results of the mechanical properties test where the best value was found in the T3 sample with a bending strength value of 104.76 kgf/cm2 and  a modulus of elasticity of 19397.1 kgf/cm2. Based on all tests, all physical properties of all samples have met the SNI 03-2105-2006 standard, while in  the bending strength test, only T3 samples have met  the SNI 03-2105-2006 standard and in the modulus of elasticity test,  all samples have not met the SNI 03-2105-2006 standard.
date: 2025-03-13
type: Thesis
type: NonPeerReviewed
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/1/Saddam%20Husein_3331200065_Fulltext.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/2/Saddam_Husein_3331200065_CP.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/3/Saddam%20Husein_3331200065_01.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/4/Saddam%20Husein_3331200065_02.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/5/Saddam%20Husein_3331200065_03.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/6/Saddam%20Husein_3331200065_04.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/7/Saddam%20Husein_3331200065_05.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/8/Saddam%20Husein_3331200065_Ref.pdf
format: text
language: en
identifier: https://eprints.untirta.ac.id/47837/9/Saddam%20Husein_3331200065_Lamp.pdf
identifier:   Husein, Saddam  (2025) STUDI PERLAKUAN CURING PADA PAPAN PARTIKEL BIODEGRADABLE PELEPAH KELAPA SAWIT BERPENGUAT MESOKARP.  S1 thesis, Fakultas Teknik Universitas Sultan Ageng Tirtayasa.