eprintid: 45358
rev_number: 53
eprint_status: archive
userid: 19252
dir: disk0/00/04/53/58
datestamp: 2025-02-05 09:55:15
lastmod: 2025-02-05 09:55:15
status_changed: 2025-02-05 09:55:15
type: thesis
metadata_visibility: show
creators_name: Permana, Yogi
creators_id: 2280200051
contributors_type: http://www.loc.gov/loc.terms/relators/THS
contributors_type: http://www.loc.gov/loc.terms/relators/THS
contributors_name: HARYADI, RUDI
contributors_name: RAMA DENNY M, YUS
contributors_id: 198101212024211001
contributors_id: 198206222009121002
corp_creators: UNIVERSITAS SULTAN AGENG TIRTAYASA
corp_creators: FAKULTAS KEGURUAN DAN ILMU PENDIDIKAN
corp_creators: JURUSAN PENDIDIKAN FISIKA
title: SINTESIS DAN KARAKTERISASI MATERIAL NaFePO4, NaMnPO4, DAN NaCoPO4 SEBAGAI KATODA PADA BATERAI NATRIUM-ION (Na-Ion)
ispublished: pub
subjects: QC
divisions: FKIP
divisions: Fisika
full_text_status: restricted
keywords: Sodium-ion battery, NaFePO₄ material, NaMnPO₄ material,
NaCoPO₄ material, ball milling
Baterai natrium ion, material NaFePO4, material NaMnPO4,
material NaCoPO4, ball milling
note: Sintesis dan karakterisasi material sebagai katoda untuk baterai natrium ion (Na-Ion) telah berhasil dilakukan dengan metode solide state reaction menggunakan prekursor NaFePO4, NaMnPO4, dan NaCoPO4 dengan suhu kalsinasi secara berturut-turut pada setiap sempel yaitu 600°C, 700°C, dan 800°C. Hasil Karakterisasi SEM dan XRD telah dilakukan untuk melihat morfologi, distribusi partikel, menganalisa struktur kristal yang terbentuk pada setiap sempel dan menentukan ukuran kristal. Dimana struktur kristal yang terbentuk dari masing-masing sampel yang telah disintesis merujuk pada struktur khas orthorhombic. sedangkan morfologi partikel yang terbentuk tidak segaram akibat terjadinya aglomerasi. Adapun untuk karakterisasi FTIR bahwa setiap sampel menununjukkan adanya puncak vibrasi (getaran) karakteristik gugus fosfat (PO₄) yang terlihat jelas, hal ini menunjukkan integrasi gugus fosfat dalam struktur kristal material katoda. Namun, Interaksi ionik dalam material menyebabkan adanya pergeseran pada posisi puncak vibrasi.
abstract: The synthesis and characterization of materials as cathodes for sodium-ion (Na-Ion) batteries were successfully conducted using the solid-state reaction method with NaFePO₄, NaMnPO₄, and NaCoPO₄ as precursors. The calcination temperatures for the samples were set sequentially at 600°C, 700°C, and 800°C. SEM and XRD analyses were carried out to investigate the morphology, particle distribution, crystal structures formed in each sample, and crystal sizes. The crystal structures of the synthesized samples were identified as distinctive orthorhombic structures. However, the particle morphology was non-uniform due to agglomeration. FTIR analysis revealed characteristic vibrational peaks of the phosphate (PO₄) group in each sample, indicating the successful integration of phosphate groups into the crystal structure of the cathode materials. However, ionic interactions within the material caused shifts in the positions of these vibrational peaks.
date: 2024
date_type: published
pages: 87
institution: UNIVERSITAS SULTAN AGENG TIRTAYASA
department: PENDIDIKAN FISIKA
thesis_type: sarjana
thesis_name: sarjana
citation:   Permana, Yogi  (2024) SINTESIS DAN KARAKTERISASI MATERIAL NaFePO4, NaMnPO4, DAN NaCoPO4 SEBAGAI KATODA PADA BATERAI NATRIUM-ION (Na-Ion).  S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.   
document_url: https://eprints.untirta.ac.id/45358/10/YOGI%20PERMANA_2280200051_FULLTEXT.pdf
document_url: https://eprints.untirta.ac.id/45358/9/YOGI%20PERMANA_2280200051_CP.pdf
document_url: https://eprints.untirta.ac.id/45358/11/YOGI%20PERMANA_2280200051_01.pdf
document_url: https://eprints.untirta.ac.id/45358/1/YOGI%20PERMANA_2280200051_02.pdf
document_url: https://eprints.untirta.ac.id/45358/2/YOGI%20PERMANA_2280200051_03.pdf
document_url: https://eprints.untirta.ac.id/45358/3/YOGI%20PERMANA_2280200051_04.pdf
document_url: https://eprints.untirta.ac.id/45358/6/YOGI%20PERMANA_2280200051_05.pdf
document_url: https://eprints.untirta.ac.id/45358/7/YOGI%20PERMANA_2280200051_REF.pdf
document_url: https://eprints.untirta.ac.id/45358/8/YOGI%20PERMANA_2280200051_LAMPIRAN.pdf