eprintid: 41551 rev_number: 22 eprint_status: archive userid: 16281 dir: disk0/00/04/15/51 datestamp: 2024-09-03 08:59:41 lastmod: 2024-09-03 08:59:41 status_changed: 2024-09-03 08:59:41 type: thesis metadata_visibility: show creators_name: Regan, Bob creators_id: 3334200083 contributors_type: http://www.loc.gov/loc.terms/relators/THS contributors_type: http://www.loc.gov/loc.terms/relators/THS contributors_name: Aziz, Abdul contributors_name: Uswatun Hasanah, Indah contributors_id: 198003072005011002 contributors_id: 199012142019032022 corp_creators: UNIVERSITAS SULTAN AGENG TIRTAYASA corp_creators: FAKULTAS TEKNIK corp_creators: TEKNIK METALURGI title: PENGARUH TEMPERATUR AUSTENISASI (900"℃" ), TEMPERING (400"℃" ) DAN PROSES PENDINGINAN TERHADAP STRUKTUR MIKRO DAN UJI TARIK PADA STAINLESS STEEL 304 THIN FOIL UNTUK APLIKASI SENSOR MOBIL ispublished: pub subjects: SJ divisions: Metalurgi full_text_status: public note: Baja paduan SS 304 merupakan baja tahan karat austenitik memiliki sifat mekanik yaitu kuat tarik sebesar 646 MPa, kuat luluh 270 MPa, perpanjangan 50%, kekerasan 82 HRB. Adapun tujuan dari penelitian kali ini yaitu untuk mengetahui pengaruh perlakuan panas stainless steel 304 thin foil yang dipanaskan dengan temperatur tinggi lalu diuji tarik untuk mengetahui struktur mikro setelah pendinginan. Adapun batasan masalah pada penelitian ini terdapat dua variabel yaitu variabel bebas dan variabel terikat. Sehingga variabel bebasnya yaitu temperatur austenisasi, temperatur tempering, dan proses pendinginan, selanjutnya variabel terikatnya yaitu ukuran butir, struktur mikro, dan uji tarik pada stainless steel 304 thin foil. Sampel uji yang telah di heat treatment menggunakan proses pendinginan cepat (quenching). Hasil penelitian menunjukan bahwa struktur mikro terlihat seperti jarum atau bilah dan memiliki warna hitam dan juga memiliki sifat mekanik yang sangat keras. Kemudian struktur mikro yang didapatkan dari pengujian ini yaitu fasa martensit dimana fasa ini terbentuk dengan memanaskan sampel hingga temperatur austenit setelah itu didinginkan cepat (quenching) dengan menggunakan air es. Selanjutnya pada proses pendinginan cepat ini tidak ada waktu bagi karbon untuk berdifusi keluar, sehingga transformasi terjadi ketika pergeseran atom dari kisi face centered cubic (FCC) menjadi body centered tetragonal (BCT). Pada sampel SUS 304 thin foil hasil uji tarik dengan ukuran butir 1,5 μm memiliki nilai true stress terkecil yaitu 406 MPa, dan memiliki nilai true strain sebesar 1. Nilai kekuatan tarik tertinggi yaitu 571 MPa, nilai true strain yaitu 1,16. Sedangkan pada sampel dengan ukuran butir 3 μm memiliki nilai true stress sebesar 380 Mpa, kemudian pada nilai true strain nya yaitu 1, sedangkan nilai kekuatan tarik tertinggi yaitu 490 MPa, dengan nilai true strain 1,16. abstract: SS 304 alloy steel is an austenitic stainless steel that has mechanical properties, namely tensile strength of 646 MPa, yield strength of 270 MPa, elongation of 50%, hardness of 82 HRB. The purpose of this research is to determine the effect of heat treatment of stainless steel 304 thin foil which is heated to high temperature and then tensile tested to determine the microstructure after cooling. As for the limitations of the problem in this study, there are two variables, namely the independent variable and the dependent variable. So that the independent variables are austenization temperature, tempering temperature, and cooling process, then the dependent variable is grain size, microstructure, and tensile test on stainless steel 304 thin foil. Test samples that have been heat treated using a rapid cooling process (quenching). The results showed that the microstructure looks like a needle or blade and has a black color and also has very hard mechanical properties. Then the microstructure obtained from this test is the martensite phase where this phase is formed by heating the sample to austenite temperature after which it is rapidly cooled (quenching) using ice water. Furthermore, in this rapid cooling process there is no time for carbon to diffuse out, so the transformation occurs when the atom shifts from face centered cubic (FCC) lattice to body centered tetragonal (BCT). In the SUS 304 thin foil sample, the tensile test results with a grain size of 1.5 μm have the smallest true stress value of 406 MPa, and have a true strain value of 1. The highest tensile strength value is 571 MPa, the true strain value is 1.16. While the sample with a grain size of 3 μm has a true stress value of 380 Mpa, then the true strain value is 1, while the highest tensile strength value is 490 MPa, with a true strain value of 1.16. date: 2024-09-02 date_type: published publication: PENGARUH TEMPERATUR AUSTENISASI (900"℃" ), TEMPERING (400"℃" ) DAN PROSES PENDINGINAN TERHADAP STRUKTUR MIKRO DAN UJI TARIK PADA STAINLESS STEEL 304 THIN FOIL UNTUK APLIKASI SENSOR MOBIL number: 88 institution: Fakultas Teknik Universitas Sultan Ageng Tirtayasa department: Teknik Metalurgi thesis_type: sarjana thesis_name: sarjana refereed: TRUE related_url_type: pub citation: Regan, Bob (2024) PENGARUH TEMPERATUR AUSTENISASI (900"℃" ), TEMPERING (400"℃" ) DAN PROSES PENDINGINAN TERHADAP STRUKTUR MIKRO DAN UJI TARIK PADA STAINLESS STEEL 304 THIN FOIL UNTUK APLIKASI SENSOR MOBIL. S1 thesis, Fakultas Teknik Universitas Sultan Ageng Tirtayasa. document_url: https://eprints.untirta.ac.id/41551/10/Bob%20Regan_3334200083_Fulltext..pdf document_url: https://eprints.untirta.ac.id/41551/2/Bob%20Regan_3334200083_01.pdf document_url: https://eprints.untirta.ac.id/41551/3/Bob%20Regan_3334200083_02.pdf document_url: https://eprints.untirta.ac.id/41551/4/Bob%20Regan_3334200083_03.pdf document_url: https://eprints.untirta.ac.id/41551/5/Bob%20Regan_3334200083_04.pdf document_url: https://eprints.untirta.ac.id/41551/6/Bob%20Regan_3334200083_05.pdf document_url: https://eprints.untirta.ac.id/41551/7/Bob%20Regan_3334200083_Ref.pdf document_url: https://eprints.untirta.ac.id/41551/8/Bob%20Regan_3334200083_Lamp.pdf document_url: https://eprints.untirta.ac.id/41551/9/Bob%20Regan_3334200083_CP..pdf