INTANDIANA, SINDA (2019) PENGARUH SELULOSA MIKROKRISTALIN TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG. S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.
![[img]](https://eprints.untirta.ac.id/style/images/fileicons/text.png) |
Text
PENGARUH SELULOSA MIKROKRISTALIN TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG.pdf Restricted to Registered users only Download (3MB) |
Abstract
Bioplastik dari pati singkong merupakan salah satu plastik biopolimer yang dapat terdegradasi oleh mikroorganisme. Tujuan dari penelitian ini adalah untuk mengetahui konsentrasi optimum selulosa mikrokristalin terhadap sifat fisik bioplastik dari pati singkong. Penelitian ini menggunakan varian konsentrasi selulosa (0%, 5%, 10%, 15% dan 20%). Untuk mengurangi kelemahan bioplastik dari pati maka dapat ditambahkan selulosa mikrokristalin. Pengujian sifat fisik dari penelitian ini adalah SEM, FTIR, TGA uji kekuatan tarik, uji densitas, uji biodegradasi, uji sudut kontak, dan uji serapan air. Hasil optimum sifat fisik diperoleh pada penambahan dengan selulosa 20% yang memiliki kekuatan tarik 16,7 MPa, serapan air 64,16% dan bahan bioplastik mudah terdegradasi karena bahan penyusun bioplastik adalah senyawa organik. Hasil penelitian menunjukkan bahwa bioplastik memiliki sifat mekanik yang baik.
| Item Type: | Thesis (S1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
|||||||||
| Additional Information: | The purpose of the research was to know optimum concentrate of microcrystalline cellulose to bioplastic physical character from cassava starch. This research used variant of cellulose concentrate (0%, 5%, 10%, 15% and 20%). Bioplastic from cassava starch is one of biopolymer plastic that can be degraded by microorganisms. To reduce the weakness of bioplastic from starch then it can be added microcrystalline cellulose. The physical characters from this research are SEM, FTIR, TGA, tensile strength, density, biodegradable, contact angle, and water uptake. Result of optimum physical character obtained addition with cellulose 20% which has tensile strength is 16,7 MPa, water uptake is 64,16% and bioplastic materials are easily degraded because the material constituent of bioplastic is an organic compound. The result indicate that bioplastic has good mechanical character. | |||||||||
| Subjects: | L Education > L Education (General) | |||||||||
| Divisions: | 02-Fakultas Keguruan dan Ilmu Pendidikan 02-Fakultas Keguruan dan Ilmu Pendidikan > 84203-Jurusan Pendidikan Fisika |
|||||||||
| Depositing User: | Admin Eprints Untirta | |||||||||
| Date Deposited: | 25 Nov 2021 11:34 | |||||||||
| Last Modified: | 25 Nov 2021 11:34 | |||||||||
| URI: | http://eprints.untirta.ac.id/id/eprint/9049 |
Actions (login required)
 |
View Item |