PENGARUH PENAMBAHAN ZINC OXIDE (ZnO) TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG

HIDAYAT, SYAMSUL (2019) PENGARUH PENAMBAHAN ZINC OXIDE (ZnO) TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG. S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.

[img] Text
PENGARUH PENAMBAHAN ZINC OXIDE (ZnO) TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG.pdf
Restricted to Registered users only

Download (4MB)

Abstract

Bioplastik merupakan polimer alami, terbuat dari material-material yang dapat terdegradasi dan dapat diperbaharui seperti pati singkong sehingga tidak akan menyebabkan masalah lingkungan. Permasalahan yang ada dalam bioplastik hingga saat ini adalah kekuatan fisikanya yang rendah sehingga akan mampu rusak dengan adanya tekanan. Penelitian ini bertujuan untuk mengetahui konsentrasi optimum Zinc Oxide (ZnO) guna memperbaiki sifat fisika bioplastik, dengan varian konsentrasi ZnO 0%, 1%, 2%, 3%, 4%, dan 5% terhadap massa total pati singkong. Pengujian sifat fisika dari penelitian ini adalah pengujuan mekanik, serta beberapa pengujian sebagai penguat data diantaranya pengujian densitas, biodegradablitas, dan struktur morfologi. Nilai optimum kekuatan tarik berada pada sampel 4% ZnO terhadap pati dengan angka 10,29 MPa. Hasil penelitian menunjukkan bahwa bioplastik memiliki sifat fisika yang baik.

Item Type: Thesis (S1)
Contributors:
ContributionContributorsNIP/NIM
Thesis advisorFirman Septiyanto, RahmatUNSPECIFIED
Thesis advisorHanif Dawam Abdullah, AkbarUNSPECIFIED
Additional Information: Bioplastics are natural polymers, made from materials that can be degraded and can be renewed like cassava starch so that they will not cause environmental problems. The problems that exist in bioplastics to date are the low physical strength that will be able to be damaged in the presence of pressure. This study aims to determine the optimum concentration of Zinc Oxide (ZnO) to improve the physical properties of bioplastics, with variants of ZnO concentrations 0%, 1%, 2%, 3%, 4%, and 5% of the total cassava starch mass. Testing the physical properties of this research is mechanical aiming, as well as some testing as a reinforcement of data including testing density, biodegradability, and morfology structure. The optimum tensile strength was in the 4% ZnO sample of starch with a figure of 10.29 MPa. The results showed that bioplastics had good physical properties.
Subjects: L Education > L Education (General)
Divisions: 02-Fakultas Keguruan dan Ilmu Pendidikan
02-Fakultas Keguruan dan Ilmu Pendidikan > 84203-Jurusan Pendidikan Fisika
Depositing User: Admin Eprints Untirta
Date Deposited: 23 Nov 2021 11:49
Last Modified: 23 Nov 2021 11:49
URI: http://eprints.untirta.ac.id/id/eprint/8963

Actions (login required)

View Item View Item