NURJANNAH, FAUZIYYAH (2019) PENGARUH FILLER SERAT RAMI TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG. S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.
![[img]](https://eprints.untirta.ac.id/style/images/fileicons/text.png) |
Text
PENGARUH FILLER SERAT RAMI TERHADAP SIFAT FISIKA BIOPLASTIK BERBAHAN DASAR PATI SINGKONG.PDF Restricted to Registered users only Download (5MB) |
Abstract
Bioplastik merupakan salah satu solusi untuk mengganti penggunaan plastikTerdapat beberapa kelamahan pada bioplastik, seperti sifat mekanik, tidak tahan terhadap air dan sifat termal yang rendah. Untuk memperbaiki kekurangan tersebut maka ditambahkanlah filler yang berupa serat rami. Serat alam rami (Boehmeria nivea) merupakan serat alam yang memiliki kekuatan tarik dan sifat lainnya yang baik diantara serat alam yang lain. Serat rami merupakan bahan pembuatan selulosa berkualitas tinggi. Pembuatan bioplastik dengan filler serat rami ini menggunakan metode dry blending dimana pada ada tiga tahapan yakni pra-mixing, mixing, dan pressing. Bioplastik dikarakterisasi dengan beberapa pengujian, dari hasil pengujian bioplastik dengan penampahan filler serat rami berpengaruh pada sifat kuat tarik dan biodegradasi bioplastik. Semakin tinggi persentase penambahan serat rami nilai kuat tarik semakin tinggi, nilai kuat tarik bioplastik 16% serat rami sebesar 17.58 MPa, dan nilai kuat tarik terkecil saat penambahan 0% serat rami yakni sebesar 3.29 MPa. Bioplastik terdegradasi dengan baik dengan penambahan serat rami pada bioplastik.
| Item Type: | Thesis (S1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
|||||||||
| Additional Information: | Bioplastics is one solution to replace the use of plastic There are some weaknesses in bioplastics, such as mechanical properties, water resistance and low thermal properties . To correct these deficiencies, a filler in the form of flax fiber is added. Natural fiber of hemp (Boehmeria nivea) is a natural fiber that has tensile strength and other properties that are good among other natural fibers. Hemp fiber is a material for making high-quality cellulose. Making bioplastics with flax fiber fillers uses dry blending method where there are three stages, namely pre-mixing, mixing, and pressing. Bioplastics are characterized by several tests, from the results of bioplastics testing with the appearance of hemp fiber fillers influencing the properties of tensile strength and biodegradation of bioplastics. The higher the percentage of hemp fiber addition the higher the tensile strength, the value of the tensile strength of bioplastic 16% hemp fiber is 17.58 MPa, and the smallest tensile strength value when the addition of 0% hemp fiber is 3.29 MPa. Bioplastics are degraded well with the addition of flax fiber to bioplastics | |||||||||
| Subjects: | L Education > L Education (General) | |||||||||
| Divisions: | 02-Fakultas Keguruan dan Ilmu Pendidikan 02-Fakultas Keguruan dan Ilmu Pendidikan > 84203-Jurusan Pendidikan Fisika |
|||||||||
| Depositing User: | Admin Eprints Untirta | |||||||||
| Date Deposited: | 22 Nov 2021 13:25 | |||||||||
| Last Modified: | 22 Nov 2021 13:25 | |||||||||
| URI: | http://eprints.untirta.ac.id/id/eprint/8847 |
Actions (login required)
 |
View Item |