Hidayat, Taufik (2013) PEMANFAATAN LIMBAH BOTTOM ASH SEBAGAI SUBSTITUSI AGREGAT HALUS DALAM PEMBUATAN BETON. S1 thesis, Fakultas teknik universitas sultan ageng tirtayasa.
![[img]](https://eprints.untirta.ac.id/style/images/fileicons/text.png) |
Text (fulltext)
1sSFVuwLoVcgisX7YxqXTNGwTuTOgsbny Restricted to Registered users only Download (278kB) |
Abstract
Penggunaan batubara sebagai sumber energi menghasilkan limbah padat berupa bottom ash danfly ash dari hasil pembakaran. Pemanfaatan limbah bottom ash khususnya yang dihasilkan oleh PT. Styrindo Mono Indonesia masih belum optimal, maka perlu dilakukan penelitian sebagai aplikasi teknologi material berkelanjutan, agar dapat mengatasi pencemaran lingkungan salah satunya sebagai bahan baku pembuatan beton. Penelitian ini membandingkan antara beton normal (tipe-A) dengan beton yang pemakaian agregat halus nya diganti oleh bottom ash, dengan variasi kondisi bottom ash yang masih alami (tipe-B), lalu kondisi dicuci dikeringkan dalam oven selama ± 24 jam (tipe-C), dan kondisi dicuci dikeringkan oleh sinar matahari (tipe-D). Jumlah benda uji beton sebanyak 60 buah, dengan variasi umur beton 7 hari, 14 hari, 21 hari, 28 hari dan 56 hari Hasil penelitian ini menyatakan limbah bottom ash dapat difungsikan sebagai substitusi agregat halus dalam pembuatan beton, dengan dicuci (dibersihkan) terlebih dahulu untuk menghilangkan kotoran-kotoran organik dan menurunkan kadar karbon. Nilai hasil pengujian pada umur 56 hari menunjukan hasil rata-rata kuat tekan beton normal (tipe A) sebesar 23,64 MPa. Tipe B mengalami penurunan nilai kuat tekan dari beton normal yaitu sebesar 20,35% dengan nilai kuat tekan sebesar 18,83 MPa. Beton tipe C menghasilkan peningkatan kuat tekan sebesar 5,09% dari beton normal dengan nilai kuat tekan yang lebih besar diantara tipe lainnya, yaitu sebesar 24,84 MPa. Beton tipe D mengalami penurunan kuat tekan sebesar 3,59% dari beton normal dengan nilai kuat tekan sebesar 22,79 MPа.
| Item Type: | Thesis (S1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
|||||||||
| Additional Information: | The use of coal as an energy source produces the form of solid waste as bottom ash and fly ash from the combustion. Particularly the use of bottom ash waste produced by PT. Styrindo Mono Indonesia is still not optimal, it is necessary to do research of the sustainable of materials technology application, in order to overcome the environmental pollution, one of them as raw for manufacturing the concrete material. This study compared between normal concrete (A-type) with the use of concrete fine aggregate which is replaced by the bottom ash, with the variety condition of natural bottom ash (B-type), then in conditions washed and dried in an oven for 24 hours (C-type), and in conditions washed and dried by the sun (Dtype). Number of concrete specimens are 60 pieces, with a variety of concrete age 7 days, 14 days, 21 days, 28 days and 56 days. Results of this study declare that the bottom ash waste can be used as a substitute for fine aggregate in the concrete production, with washed (cleaned) in advance to remove organic impurities and dirt-lowering levels of carbon. Value of the test results at the age of 56 days showed an average yield the compressive strength for normal concrete (A-type) is 23.64 MPa. Type B has decreased the compressive strength of normal concrete is equal of 20.35% with the compressive strength is 18.83 MPa. The C-type concrete compressive strength increased by 5,09% of the normal concrete with the compressive strength greater among the other types, that is 24.84 MPa. The D-type concrete compressive strength decreased by 3.59% of normal concrete with the compressive strength is 22,79 MPa. | |||||||||
| Uncontrolled Keywords: | Beton, Kuat Tekan, Bottom Ash | |||||||||
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) T Technology > TH Building construction |
|||||||||
| Divisions: | 03-Fakultas Teknik > 22201-Jurusan Teknik Sipil | |||||||||
| Depositing User: | SISWA MAGANG FT | |||||||||
| Date Deposited: | 17 Sep 2025 02:12 | |||||||||
| Last Modified: | 17 Sep 2025 02:12 | |||||||||
| URI: | http://eprints.untirta.ac.id/id/eprint/54675 |
Actions (login required)
 |
View Item |