Fidarohman, Fidarohman (2022) Eliminasi limbah ciprofloxacin menggunakan kombinasi proses elektrokoagulasi dan fotokatalisis dengan TiO2 nanotubes yang disensitasi oleh antosianin. Master thesis, universitas sultan ageng tirtayasa.

	Text Fidarohman_7780200001_Fulltext.pdf Restricted to Registered users only Download (2MB)
	Text Fidarohman_7780200001_CP.pdf Restricted to Registered users only Download (10MB)
	Text Fidarohman_7780200001_01.pdf Restricted to Registered users only Download (777kB)
	Text Fidarohman_7780200001_02.pdf Restricted to Registered users only Download (580kB)
	Text Fidarohman_7780200001_03.pdf Restricted to Registered users only Download (225kB)
	Text Fidarohman_7780200001_04.pdf Restricted to Registered users only Download (1MB)
	Text Fidarohman_7780200001_05.pdf Restricted to Registered users only Download (62kB)
	Text Fidarohman_7780200001_Ref.pdf Restricted to Registered users only Download (179kB)
	Text Fidarohman_7780200001_Lamp.pdf Restricted to Registered users only Download (462kB)

Abstract

Salah satu metode potensial untuk pengolahan limbah antibiotik ciprofloxacin (CIP) yang murah, efektif, dan ramah lingkungan adalah metode fotokatalisis dengan menggunakan semikonduktor TiO2. Akan tetapi TiO2 ini memiliki beberapa kelemahan diantaranya luas permukaan spesifiknya yang kecil, laju rekombinasi yang besar, serta nilai energi band gap yang tinggi. Beberapa kelemahan tersebut mengakibatkan penyerapan foton rendah. Untuk meningkatkan efisiensi fotokatalis TiO2 pada penelitian ini dilakukan modifikasi morfologi menjadi nanotubes dan penambahan sensitizer antosianin. Untuk meningkatkan efektifitas eliminasi CIP yaitu dengan mengkombinasikan metode fotokatalisis dan elektrokoagulasi. Tujuan penelitian ini adalah untuk mendapatkan sintesis dan karakterisasi fotokatalis TiO2 nanotubes dengan penambahan sensitizer antosianin, mendapatkan kondisi terbaik kombinasi proses elektrokoagulasi-fotokatalisis untuk eliminasi CIP dan mendapatkan kondisi optimum dengan penambahan sensitizer antosianin pada kombinasi proses elektrokoagulasi-fotokatalisis. Sintesis TiO2 nanotubes menggunakan metode anodisasi dengan menggunakan elektrolit gliserol dengan komposisi 0,5% wt NH4F, 25% vol air. Proses elektrokoagulasi menggunakan katoda SS 316 dan aluminium sebagai anoda. Karakterisasi TiO2 yang dihasilkan menggunakan SEM, XRD dan UV-Vis DRS. Konsentrasi CIP diukur menggunakan spektrofotometer. Hasil penelitian yang telah dilakukan, karakterisasi fotokatalis TiO2 nanotubes dengan penambahan sensitizer antosianin tidak merubah struktur morfologi TNTAs. Proses elektrokoagulasi kondisi terbaik pada voltase 50 volt dekolorisasi CIP dengan konsentrasi awal 10 ppm mencapai 71,98%. Sedangkan pada proses fotokatalisis diperoleh pada komposisi kadar air 25% dan 50 volt. Tanpa antosianin dapat mendegradasi CIP sebesar 56,44%, sedangkan dengan antosianin sebesar 64,28%. Kondisi optimum kombinasi proses elektrokoagulasi-fotokatalisis pada pH 9 dapat meningkatkan eliminasi CIP dengan menggunakan TNTAs tanpa antosianin menghasilkan 86,28%. Dengan TNTAs yang dilapisi sensitizer antosianin dapat meningkatkan eliminasi CIP hingga 95,77%.

Item Type:	Thesis (Master)
Additional Information:	One of the potential methods for the cheap, effective, and environmentally friendly treatment of ciprofloxacin antibiotic waste (CIP) is the photocatalysis method using TiO2 semiconductors. However, TiO2 has several disadvantages including a small specific surface area, a large recombination rate, and a high band gap energy value. Some of these drawbacks result in low photon absorption. To improve the efficiency of TiO2 photocatalysts in this study, morphological modifications were carried out into nanotubes and the addition of anthocyanin sensitizers. To increase the effectiveness of CIP elimination, namely by combining photocatalysis and electrocoagulation methods. The purpose of this study is to obtain the synthesis and characterization of photocatalyst TiO2 nanotubes with the addition of anthocyanin sensitizers, obtain the best conditions of the combination of electrocoagulation-photocatalysis processes for the elimination of CIP and obtain optimum conditions by the addition of anthocyanin sensitizers in the combination of electrocoagulation-photocatalysis processes. Synthesis of TiO2 nanotubes using anodization method using glycerol electrolyte with a composition of 0.5% wt NH4F, 25% vol water. The electrocoagulation process uses the SS 316 cathode and aluminum as the anode. Characterization of the resulting TiO2 using SEM, XRD and UV-Vis DRS. CIP concentrations are measured using a spectrophotometer. The results of the studies that have been carried out, photocatalyst characterization of TiO2 nanotubes with the addition of an anthocyanin sensitizer does not change the morphological structure of TNTAs. The electrocoagulation process was best condition at a voltage of 50 volts decolorization of CIP with an initial concentration of 10 ppm reaching 71.98%. While in the photocatalysis process obtained at a composition of water content of 25% and 50 volts. Without anthocyanins, it can degrade CIP by 56.44%, while with anthocyanins by 64.28%. The optimum condition of the combination of electrocoagulation-photocatalysis processes at pH 9 can improve the elimination of CIP using TNTAs without anthocyanins resulting in 86.28%. With TNTAs coated with anthocyanin sensitizer can increase CIP elimination by up to 95.77%.
Uncontrolled Keywords:	antosianin, ciprofloxacin, elektrokoagulasi-fotokatalisis, fotokatalisis, TiO2 nanotubes anthocyanins, ciprofloxacin, electrocoagulation and photocatalysis, photocatalysis, TiO2 nanotubes
Subjects:	T Technology > TP Chemical technology
Divisions:	08-Pascasarjana > 84104-Magister Teknik Kimia
Depositing User:	fida Fida
Date Deposited:	07 Feb 2023 10:08
Last Modified:	07 Feb 2023 10:08
URI:	http://eprints.untirta.ac.id/id/eprint/21270

Actions (login required)

View Item