High-strength aluminum alloy of ultrafine grained by consolidation-ECAP

Pramono, Agus High-strength aluminum alloy of ultrafine grained by consolidation-ECAP. IOP Conference Series: Materials Science and Engineering.

[img] Text
consolidation ECAP_Agus 3.pdf

Download (1MB)
[img] Text
consolidation ECAP_Agus 3.pdf.pdf

Download (2MB)
[img] Image
KRSPONDNS_consolidation-ECAP.png

Download (409kB)

Abstract

Technology of Severe Plastic Deformation (SPD) has emerged as a widely known procedure for the fabrication of ultrafine grained metals and alloys. Equal Channel Angular Pressing (ECAP) are one of methods of SPD has been developed for many applications; military devices, aerospace and automotive components. This paper examines recent developments related to the use powder of Aluminum alloys processed by consolidation-ECAP, for grain refinement; Al-5Mg, were compared by another type of Aluminum, which has also been researched. Characterization by mechanical, physical and microstructured. In the current study powder of material wrapped in copper capsule to be compressed and heated at a temperature of 400°C in hot press under the pressure of 450-500 MPa. Afterward the powder in solid condition was cooled in the air. The sample results of Aluminum by ECAP process then followed heat treatment with type Annealed, for heating at a temperature of 346°C for 1,5 continuing 415°C during 2 hours followed by heating at a temperature of 205-230°C for 4 hours. This paper describes the effect of heat treatment on the characteristics of the powder material on Al-5Mg are based on changes in the mechanical properties and microstructures.

Item Type: Article
Subjects: Q Science > Q Science (General)
T Technology > TN Mining engineering. Metallurgy
Divisions: 03-Fakultas Teknik > 27201-Jurusan Teknik Metalurgi
Depositing User: Perpustakaan FT
Date Deposited: 27 Sep 2022 15:19
Last Modified: 27 Sep 2022 15:19
URI: http://eprints.untirta.ac.id/id/eprint/15881

Actions (login required)

View Item View Item