HAFIEDH, ABDUL (2015) PERENCANAAN BETON MUTU TINGGI DENGAN MENGGUNAKAN PORTLAND COMPOSITE CEMENT (PCC) DAN HR-WATER REDUCER LIGNO P 100 DAN BAHAN TAMBAH ABU SEKAM PADI. S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.
![[img]](https://eprints.untirta.ac.id/style/images/fileicons/text.png) |
Text
PERENCANAAN BETON MUTU TINGGI DENGAN.pdf - Published Version Restricted to Registered users only Download (6MB) |
Abstract
Cairan Ligno P-100 merupakan jenis Superplasticizer tipe polycarbonate ethers murni yang memiliki kemampuan accelerator dan HR-water�reducer/superplasticizer. Dalam penelitian ini cairan Ligno P-100 dicampur degan abu sekam padi sebagai bahan tambah pembuatan beton. Penelitian ini bertujuan untuk mengoptimalkan pemanfaatan limbah abu sekam padi sebagai bahan tambah pembuatan beton. Penelitian ini merencanakan beton mutu tinggi dengan menggunakan admixture Portland Composite Cement (PCC) dan HR-WR Ligno P-100 dan Bahan Tambah Abu Sekam Padi dengan variasi dosis 1,25% Ligno dan 10% abu sekam padi, 1,5% Ligno dan 10% abu sekam padi, 1,75% Ligno dan 10% abu sekam padi, 2% Ligno dan 10% abu sekam padi. Jumlah benda uji sebanyak 48 buah, dengan variasi umur beton 3 hari, 7 hari, 14 hari dan 28 hari. Hasil penelitian ini menyatakan penambahan zat aditif Ligno P-100 dapat mempengaruhi kemudahan pengerjaan beton dan menunjukan abu sekam padi tidak berpengaruh signifikan terhadap kuat tekan beton. Nilai hasil rata-rata kuat tekan pada umur 28 hari untuk beton yang menggunakan dosis 1,25% Ligno dan 10% abu sekam padi sebesar 39,84 MPa, dosis 1,5% Ligno dan 10% abu sekam padi sebesar 40,26 MPa, dosis 1,75% Ligno dan 10% abu sekam padi sebesar 40,68 Mpa, dosis 2% Ligno dan 10% abu sekam padi sebesar 42,11 MPa. Kuat tekan beton pada penelitian ini memenuhi persyaratan untuk beton mutu tinggi tetapi tidak mencapai kuat tekan rencana.
| Item Type: | Thesis (S1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
|||||||||
| Additional Information: | Liquid Ligno P-100 is one of superplasticizer type polycarbonatethers pure that has the ability for accelerator and HR water reducer or superplasticizer. In this research, Liquid Ligno P-100 will mixed by Rice Husk Ash as the admixture for concrete. This research plan high-quality concrete admixture using HR-WR Ligno P 100, Portland Composite Cement (PCC) and rice husk ash with variations in doses 1,25 % Ligno P100 and 10% husk ash, 1,50 % Ligno P100 and 10% husk ash, 1,75 % Ligno P100 and 10% husk ash, 2 % Ligno P100 and 10% husk ash. The number of test objects as much as 48 pieces, with variations in the concrete age 3 day, 7 day, 14 day and 28 day. The results of this research said the addition of these additives can affect the ease of workmanship of the concrete and the rice husk ash in this research not very affected to the value of concrete strength. The value of the average results strong press at the age of 28 days for the concrete using a dose of 1.25% Ligno and 10% rice husk ash of 39.84 MPa, dosage 1.5% Ligno and 10% rice husk ash of 40.26 MPa, 1.75% Ligno and 10% rice husk ash of 40.68 MPa, and the dosage of 2% Ligno and 10% rice husk ash 42.11 MPa. Compressive strength of concrete in this research meet the requirements for high quality concrete, but did not achieve to strong press of the plan. | |||||||||
| Uncontrolled Keywords: | Kata Kunci : Ligno P-100, Abu Sekam Padi, Portland Composite Cement, Beton Mutu Tinggi. | |||||||||
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) | |||||||||
| Divisions: | 03-Fakultas Teknik > 22201-Jurusan Teknik Sipil | |||||||||
| Depositing User: | Perpustakaan Pusat | |||||||||
| Date Deposited: | 21 Apr 2022 14:44 | |||||||||
| Last Modified: | 22 Aug 2022 14:02 | |||||||||
| URI: | http://eprints.untirta.ac.id/id/eprint/12725 |
Actions (login required)
 |
View Item |