ISMAIL, M. ISA (2014) PERENCANAAN BETON MUTU TINGGI DENGAN MENGGUNAKAN HR-WATER REDUCER LIGNO P 100 DAN PORTLAND COMPOSITE CEMENT (PCC). S1 thesis, UNIVERSITAS SULTAN AGENG TIRTAYASA.
![[img]](https://eprints.untirta.ac.id/style/images/fileicons/text.png) |
Text
PERENCANAAN BETON MUTU TINGGI DENGAN MENGGUNAKAN HR-WATER REDUCER LIGNO P 100.pdf - Published Version Restricted to Registered users only Download (6MB) |
Abstract
Penelitian ini membahas tentang kuat tekan beton mutu tinggi yang menggunakan zat aditif HR-Water Raducer Ligno P 100 dan Portland Composite Cement (PCC). Permasalahan yang sangat berpengaruh pada kuat tekan beton adalah adanya porositas, untuk mengatasi permasalahan tersebut dapat memgunakan Superplasticizer cairan Ligno P 100 yang sifatnya dapat mengurangi air tetapi mudah dikerjakan dan penelitian ini memakai Portland Composite Cement merek Semen Padang yang mengoptimalkan klinker dilakukan dengan penambahan bahan aktif seperti pozzolan, fly-ash dan bahan lain yang berfungsi memperbaiki daya rekat. Penelitian ini merencanakan beton mutu tinggi dengan menggunakan zat aditif HR-WR Ligno P 100 dan Portland Composite Cement (PCC) dengan variasi kadar zat aditif HR-WR Ligno P 100 0.8%, 1.2%, 1.6% dan 2%. Jumlah benda uji sebanyak 48 buah, dengan umur beton 3 hari, 7 hari, 14 hari dan 28 hari. Hasil penelitian ini membuktikan penambahan zat aditif ini dapat mempengaruhi kemudahan pengerjaan beton karena memiliki sifat kecairan (fluidity) yang tinggi sehingga dapat mengurangi waktu proses pemadatan. Nilai hasil rata-rata kuat tekan pada umur 28 hari untuk beton yang menggunakan kadar 0,8% sebesar 37,25 MPa, kadar 1,2% sebesar 36,52 MPa, kadar 1,6% sebesar 35,42 MPa, dan kadar 2% sebesar 40,31 MPa. Hasil kuat tekan optimum HR-WR Ligno P 100 didapat pada kadar 2% sebesar 40,31 MPa.
| Item Type: | Thesis (S1) | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Contributors: |
|
|||||||||
| Additional Information: | This reasearch discusses about high compressive high strength concrete with additives using HR-Water Raducer Ligno P 100 and Portland Composite Cement (PCC). The problem is very influential on strong press concrete are the presence of porosity. Overcome with the probems it could be used fluid superplatisizer Ligno P 100 have characteristic able to reduce water but easily worked in this rasearch used Semen Padang potrland composite cement which optimize clinker by adding active materials such as pozzolan, fly ash and other materials has characteristics to repair adhesion. This reasearch was designed high strength concrete used HR-water reducer Ligno P 100 and portland composite cement (PCC) with variuos mixtures ratio 0,8%, 1,2%, 1,6% and 2% of HR-Water Reducer Ligno P 100. Number of specimen 48 pieces with concrete age 3 days, 7 days, 14 days and 28 days. The result from this reasearch proved that adding additives affect the easily worked of concrete because the high fluidity so it can reduced processing time of compaction. Result of compressive strenghth in 28 days wiht mixtures ratio 0,8%, 1,2%, 1,6% and 2% are 37,25 MPa; 36,52 MPa; 35,42 MPa; and 40,31 MPa. The result of optimum compressive strength HR-WR Ligno P 100 obtained in content of 2% at 40.31 MPa | |||||||||
| Uncontrolled Keywords: | Kata Kunci: Water Reducer, Superplasticizer, Beton Mutu Tinggi, Kuat Tekan, Portland Composite Cement | |||||||||
| Subjects: | T Technology > TA Engineering (General). Civil engineering (General) | |||||||||
| Divisions: | 03-Fakultas Teknik > 22201-Jurusan Teknik Sipil | |||||||||
| Depositing User: | Perpustakaan Pusat | |||||||||
| Date Deposited: | 21 Apr 2022 14:44 | |||||||||
| Last Modified: | 22 Aug 2022 10:45 | |||||||||
| URI: | http://eprints.untirta.ac.id/id/eprint/12723 |